An ageing Resistant Bio-Medically Competent Zirconia Ceramics for Hip Implant
tm3296913940
Category of Technology / Product
  • Description
  • Intellectual Property
  • Corporate Information
  • Contact

The effectiveness of MNO2 and AL203 in enhancing the mechanical properties and retarding the low temperature degradation of Y-TZP was evaluated by pressureless sintering at a sintering temperature of 1250C - 1550C using the standard 2 hours holding time. It was revealed that the additions of MNO2 and AL203 to Y-TZP were beneficial for sintering, mechanical properties and hydrothermal ageing resistance. The optimum level of doping was found to be 0.6WT% MNO2/0.4WT% AL203.

Industrial Design
No
Trademarks
No
Patent
No
Other IP Protection
No
Organization Name
Organization Category
Address

Universiti Tenaga Nasional, Block Administration, Jalan Serdang, Seksyen 11
43650 Bandar Baru Bangi
Selangor
Malaysia

Full Name [1]
Meenaloshini A/P Satgunam
Email [1]
meenaloshini@uniten.edu.my